X5 Hot-Slip Low Temperature Shrink Film
X5 is a kind of heat shrinkable film with excellent performance, which helps to solve almost all problems encountered in the process of shrinkage. It has very good shrinkage at low temperature, and with high shrink speed and good sealing strength. As X5 film has more than 70% of shrinkage, it brings best packaging effect even under the worst conditions. X5 has a good slip property, and can be used for folding box or flat sheet articles after shrink packaging, without adhesion or abrasion. In addition, X5 also has the advantages of wide shrinkage temperature range, good heat sealing performance and low shrinkage force, compared to all other non cross-linked polyolefin shrink film.
X5 is suitable for any packaging machine.
Thickness: 9um, 11um, 14um, 19um.
Product Application
Performance Parameters
| TEST ITEM | UNIT | ASTM TEST | TYPICAL VALUES | |||||||||
| GAUGE 厚度 | 9um | 11um | 14um | 19um | ||||||||
| TENSILE | ||||||||||||
| Tensile Strength (MD) 拉伸强度 | N/mm² | D882 | 115 | 115 | 110 | 95 | ||||||
| Tensile Strength (TD) | 110 | 110 | 105 | 95 | ||||||||
| Elongation(MD) 断裂伸长率 | % | 95 | 100 | 105 | 100 | |||||||
| Elongation (TD) | 90 | 95 | 100 | 95 | ||||||||
| TEAR 撕裂强度 | ||||||||||||
| MD at 400gm | gf | D1922 | 6.5 | 8.5 | 12.5 | 15.5 | ||||||
| TD at 400gm | 6.2 | 9.5 | 13.5 | 16.5 | ||||||||
| SEAL STRENGTH 热封强度 | ||||||||||||
| MD\Hot Wire Seal | N/mm | F88 | 0.6 | 0.75 | 0.88 | 0.95 | ||||||
| TD\Hot Wire Seal | 0.65 | 0.75 | 0.93 | 1.1 | ||||||||
| COF (Film To Film) | - | |||||||||||
| Static 静摩擦 | D1894 | 0.16 | 0.15 | 0.15 | 0.18 | |||||||
| Dynamic 动摩擦 | 0.16 | 0.15 | 0.12 | 0.18 | ||||||||
| Dynamic(HotSlip)@60℃ 热动摩擦 | 0.28 | 0.26 | 0.23 | 0.22 | ||||||||
| OPTICS | ||||||||||||
| Haze 雾度 | D1003 | 3.2 | 3.5 | 3.8 | 4.0 | |||||||
| Clarity 透明度 | % | D1746 | 98.5 | 98.0 | 97.5 | 97.0 | ||||||
| Gloss @ 45Deg 光泽度 | D2457 | 82 | 82.0 | 84.0 | 84.0 | |||||||
| BARRIER 阻隔性 | ||||||||||||
| Oxygen Transmission Rate 透氧率 | cc/㎡/day | D3985 | 14400 | 11800 | 11700 | 9600 | ||||||
| Water Vapor Transmission Rate 透水气率 | gm/㎡/day | F1249 | 55 | 48 | 45 | 38 | ||||||
| SHRINKAGE PROPERTIES 收缩性 | MD | TD | MD | TD | ||||||||
| Free Shrinkage 收缩率 | 80℃ | % | D2732 | 16.5 | 24.5 | 15.5 | 24.0 | |||||
| 90℃ | 25.0 | 31.5 | 24.5 | 31.5 | ||||||||
| 100℃ | 35.0 | 43.5 | 34.0 | 43.0 | ||||||||
| 110℃ | 52.0 | 55.0 | 51.0 | 54..0 | ||||||||
| 120℃ | 64.0 | 66.0 | 63.0 | 65.5 | ||||||||
| 130℃ | 71.0 | 70.0 | 70.5 | 70.0 | ||||||||
| MD | TD | MD | TD | |||||||||
| Shrink Tension 收缩张力 | 80℃ | 1.45 | 1.75 | 1.60 | 1.85 | |||||||
| 90℃ | Mpa | D2838 | 1.85 | 2.10 | 1.95 | 2.25 | ||||||
| 100℃ | 2.15 | 2.35 | 2.25 | 2.40 | ||||||||
| 110℃ | 2.50 | 2.75 | 2.65 | 2.80 | ||||||||
| 120℃ | 2.70 | 2.80 | 2.85 | 2.95 | ||||||||
| 130℃ | 2.45 | 2.55 | 2.65 | 2.75 | ||||||||
Note:This information represents our best judgment on the work done, but the company assumes no liability whatsoever in connection with the use of information or findings contained herein.