10" Cross Linked Polyolefin Centerfold Shrink Film
10" cross-linked polyolefin centerfold shrink film is produced using high quality polyolefin materials, centerfold shrink film with high transparency and excellent shrink performance, can be used for a variety of shapes and sizes of items, and high protection, not easy to break.
Product Details
It can be used to package food, multi-piece combination packages, daily necessities, electronic products and so on.
Performance Parameters
| TEST ITEM | UNIT | ASTM TEST | TYPICAL VALUES | |||||||||
| GAUGE 厚度 | 10um | 11um | 15um | 19um | ||||||||
| TENSILE | ||||||||||||
| Tensile Strength (MD) 拉伸强度 | N/mm² | D882 | 130 | 125 | 120 | 115 | ||||||
| TensileStrength (TD) | 125 | 120 | 115 | 110 | ||||||||
| Elongation(MD) 断裂伸长率 | % | 105 | 105 | 110 | 110 | |||||||
| Elongation(TD) | 100 | 100 | 105 | 105 | ||||||||
| TEAR 撕裂强度 | ||||||||||||
| MDat 400gm | gf | D1922 | 9.0 | 10.0 | 12.0 | 15.5 | ||||||
| TDat 400gm | 8.0 | 9.5 | 11.5 | 14.5 | ||||||||
| SEALSTRENGTH 热封强度 | ||||||||||||
| MD\HotWire Seal | N/mm | F88 | 0.75 | 0.80 | 0.95 | 1.15 | ||||||
| TD\HotWire Seal | 0.80 | 0.85 | 0.98 | 1.25 | ||||||||
| COF(Film To Film) | - | |||||||||||
| Static 静摩擦 | D1894 | 0.38 | 0.35 | 0.32 | 0.30 | |||||||
| Dynamic 动摩擦 | 0.38 | 0.35 | 0.33 | 0.30 | ||||||||
| OPTICS | ||||||||||||
| Haze 雾度 | D1003 | 1.7 | 1.9 | 2.2 | 2.5 | |||||||
| Clarity 透明度 | D1746 | 99.0 | 99.0 | 98.5 | 97.5 | |||||||
| Gloss@ 45Deg 光泽度 | D2457 | 88.5 | 88.0 | 87.5 | 87.5 | |||||||
| BARRIER 阻隔性 | ||||||||||||
| OxygenTransmission Rate 透氧率 | cc/㎡/day | D3985 | 14500 | 13200 | 10800 | 7300 | ||||||
| Water Vapor Transmission Rate 透水气率 | gm/㎡/day | F1249 | 52.4 | 47.5 | 35.5 | 27.5 | ||||||
| SHRINKAGEPROPERTIES 收缩性 | MD | TD | MD | TD | ||||||||
| Free Shrinkage 收缩率 | 100℃ | % | D2732 | 18 | 25 | 17 | 23 | |||||
| 110℃ | 32 | 40 | 30 | 38 | ||||||||
| 120℃ | 55 | 58 | 55 | 57 | ||||||||
| 130℃ | 65 | 66 | 66 | 67 | ||||||||
| MD | TD | MD | TD | |||||||||
| Shrink Tension 收缩张力 | 100℃ | Mpa | D2838 | 1.65 | 2.45 | 1.75 | 2.55 | |||||
| 110℃ | 2.85 | 3.65 | 2.90 | 3.55 | ||||||||
| 120℃ | 2.95 | 3.95 | 3.20 | 4.00 | ||||||||
| 130℃ | 2.75 | 3.40 | 2.60 | 3.20 | ||||||||