ZDF08 Economical Cross-Linked Film
With cross-link technology, ZDF08 is a perfect combination of performance and yield. This film is suitable for nearly all sealing systems because of its high strength and high seal-ability. The higher yielding gauges provide lower film cost per package and the efficiencies of fewer roll changes. ZDF08 is our high yield equivalent to ZDF03.
Available thickness: 10 micron, 13 micron,,17 micron, 22 micron
Product Application
Performance Parameters
| TEST ITEM | UNIT | ASTM TEST | TYPICAL VALUES | ||||||||
| GAUGE 厚度 | 10um | 13.5um | 17um | 22um | |||||||
| TENSILE | |||||||||||
| Tensile Strength (MD) 拉伸强度 | N/mm² | D882 | 130 | 130 | 130 | 125 | |||||
| TensileStrength (TD) | 125 | 125 | 125 | 120 | |||||||
| Elongation(MD) 断裂伸长率 | % | 110 | 115 | 120 | 120 | ||||||
| Elongation(TD) | 105 | 110 | 110 | 115 | |||||||
| TEAR 撕裂强度 | |||||||||||
| MDat 400gm | g | D1922 | 9 | 14.0 | 16.5 | 22.5 | |||||
| TDat 400gm | 9.5 | 13.0 | 18.5 | 23.5 | |||||||
| SEALSTRENGTH 热封强度 | |||||||||||
| MD\HotWire Seal | N/mm | F88 | 0.95 | 1.20 | 1.25 | 1.50 | |||||
| TD\HotWire Seal | 1.05 | 1.35 | 1.45 | 1.65 | |||||||
| COF(Film To Film) | - | ||||||||||
| Static 静摩擦 | D1894 | 0.24 | 0.21 | 0.18 | 0.19 | ||||||
| Dynamic 动摩擦 | 0.24 | 0.21 | 0.18 | 0.19 | |||||||
| OPTICS | |||||||||||
| Haze 雾度 | D1003 | 2.2 | 2.4 | 2.6 | 2.9 | ||||||
| Clarity 透明度 | D1746 | 98.5 | 98.5 | 98.0 | 98.0 | ||||||
| Gloss@ 45Deg 光泽度 | D2457 | 89.0 | 88.5 | 88.0 | 86.5 | ||||||
| BARRIER 阻隔性 | |||||||||||
| OxygenTransmission Rate 透氧率 | cc/㎡/day | D3985 | 12100 | 9700 | 7400 | 6800 | |||||
| WaterVapor Transmission Rate 透水气率 | gm/㎡/day | F1249 | 40.5 | 32.5 | 25.5 | 19.5 | |||||
| SHRINKAGEPROPERTIES 收缩性 | MD | TD | |||||||||
| Free Shrinkage 收缩率 | 100℃ | % | D2732 | 19 | 28 | ||||||
| 110℃ | 37 | 45 | |||||||||
| 120℃ | 70 | 72 | |||||||||
| 130℃ | 81 | 79 | |||||||||
| MD | TD | ||||||||||
| Shrink Tension 收缩张力 | 100℃ | Mpa | D2838 | 2.20 | 2.65 | ||||||
| 110℃ | 2.65 | 3.80 | |||||||||
| 120℃ | 2.85 | 4.00 | |||||||||
| 130℃ | 2.80 | 3.90 | |||||||||
Note:This information represents our best judgment on the work done, but the company assumes no liability whatsoever in connection with the use of information or findings contained herein.
以上资料是本公司内部评测之数据，仅供参考。