ZCR03 PCR Cross-Linked Shrink Film
This is a kind of polyolefin cross-linked heat shrinkable film contains 31% of post consumer recycled material.
In addition to using PCR returns, ZCR03 and ZDF03 are basically the same in terms of production process, so their properties are also very similar, and they also have the advantages of high shrinkage (nearly 80%), good mechanical properties, high heat sealing strength, good toughness, and outstanding heat and cold resistance.
ZCR03 film has passed the GRS4.0 certification (global recycling standard certification).
Thickness: 15um, 19um, 25um.
| TEST ITEM | UNIT | ASTM TEST | TYPICAL VALUES | |||||||||
| INTRODUCTION | ||||||||||||
| Post Consumer Recycling | 31%Recycled post-consumer polyethylene(RM0193) | |||||||||||
| Gauge 厚度 | 15um | 19um | 25um | 30um | ||||||||
| TENSILE | ||||||||||||
| Tensile Strength (MD) 拉伸强度 | N/mm² | D882 | 130 | 125 | 120 | 115 | ||||||
| Tensile Strength (TD) | 115 | 110 | 110 | 110 | ||||||||
| Elongation(MD) 断裂伸长率 | % | 125 | 115 | 125 | 120 | |||||||
| Elongation (TD) | 110 | 110 | 110 | 100 | ||||||||
| TEAR 撕裂强度 | ||||||||||||
| MD at 400gm | gf | D1922 | 11.5 | 14.3 | 16.7 | 21.5 | ||||||
| TD at 400gm | 9.8 | 14.8 | 17.2 | 23.4 | ||||||||
| SEAL STRENGTH 热封强度 | ||||||||||||
| MD\Hot Wire Seal | N/mm | F88 | 1.20 | 1.40 | 1.55 | 1.95 | ||||||
| TD\Hot Wire Seal | 1.40 | 1.55 | 1.65 | 2.05 | ||||||||
| COF (Film To Film) | - | |||||||||||
| Static 静摩擦 | D1894 | 0.20 | 0.18 | 0.22 | 0.23 | |||||||
| Dynamic 动摩擦 | 0.20 | 0.18 | 0.22 | 0.23 | ||||||||
| OPTICS | ||||||||||||
| Haze 雾度 | D1003 | 3.2 | 3.6 | 4.0 | 4.5 | |||||||
| Clarity 透明度 | D1746 | 92.5 | 91.5 | 90.5 | 90.0 | |||||||
| Gloss @ 45Deg 光泽度 | D2457 | 85.0 | 84.0 | 82.0 | 81.0 | |||||||
| BARRIER 阻隔性 | ||||||||||||
| Oxygen Transmission Rate 透氧率 | cc/㎡/day | D3985 | 8800 | 7500 | 5100 | 3900 | ||||||
| Water Vapor Transmission Rate 透水气率 | gm/㎡/day | F1249 | 23.5 | 19.4 | 11.6 | 9.2 | ||||||
| SHRINKAGEPROPERTIES 收缩性 | MD | TD | MD | TD | ||||||||
| Free Shrinkage 收缩率 | 100℃ | % | D2732 | 14.0 | 22.5 | 13.0 | 22.0 | |||||
| 110℃ | 36.5 | 45.0 | 33.0 | 44.5 | ||||||||
| 120℃ | 73.0 | 71.5 | 70.5 | 70.0 | ||||||||
| 130℃ | 81.0 | 80.0 | 81.0 | 80.0 | ||||||||
| MD | MD | TD | TD | |||||||||
| Shrink Tension 收缩张力 | 100℃ | Mpa | D2838 | 2.05 | 2.35 | 1.70 | 2.25 | |||||
| 110℃ | 2.75 | 3.65 | 2.65 | 3.45 | ||||||||
| 120℃ | 3.15 | 4.05 | 2.95 | 3.65 | ||||||||
| 130℃ | 3.00 | 3.65 | 2.75 | 3.20 | ||||||||
Note:This information represents our best judgment on the work done, but the company assumes no liability whatsoever in connection with the use of information or findings contained herein.
以上资料是本公司内部评测之数据，仅供参考。
FAQ
Q: What is cross linked shrink film?
A: Cross-linked shrink film is a type of plastic shrink film that has been treated with a process called cross-linking, which makes it more durable and resistant to punctures and tears. It is commonly used for packaging food items, electronics, and other consumer goods.
Q: What is cross linked film?
A: Cross-linked film is a type of plastic film that has been treated with a process called cross-linking, which creates a molecular network between the polymer chains. This can improve the physical properties of the film, such as its strength, durability, and resistance to heat and chemicals. Cross-linked films are often used in applications where high performance and long-term durability are required, such as in construction, aerospace, and automotive industries.