ZCR01 PCR Polyolefin Shrink Film
This is a polyolefin shrink film contains 30% of post consumer recycled material. In addition to using a large number of PCR returns, this film has the same production process as ZDF01, with basically same properties and application. It also has the advantages of good mechanical properties, good heat sealing, high shrinkage, and good adaptability to various packaging machines.
The film has passed the GRS4.0 certification (global recycling standard certification).
Thickness: 15um, 19um, 25um.
Product Application
Performance Parameters
| TEST ITEM | UNIT | ASTM TEST | TYPICAL VALUES | |||||||||
| INTRODUCTION | ||||||||||||
| Post Consumer Recycling | 30%Recycled post-consumer polyethylene(RM0193) | |||||||||||
| Gauge 厚度 | 15um | 19um | 25um | 30um | ||||||||
| TENSILE | ||||||||||||
| Tensile Strength (MD) 拉伸强度 | N/mm² | D882 | 115 | 110 | 90 | 88 | ||||||
| Tensile Strength (TD) | 110 | 105 | 85 | 80 | ||||||||
| Elongation(MD) 断裂伸长率 | % | 105 | 110 | 105 | 100 | |||||||
| Elongation (TD) | 100 | 105 | 95 | 90 | ||||||||
| TEAR 撕裂强度 | ||||||||||||
| MD at 400gm | gf | D1922 | 10.5 | 13.5 | 16.5 | 20.5 | ||||||
| TD at 400gm | 9.8 | 12.5 | 16.5 | 22.5 | ||||||||
| SEAL STRENGTH 热封强度 | ||||||||||||
| MD\Hot Wire Seal | N/mm | F88 | 0.85 | 0.95 | 1.15 | 1.35 | ||||||
| TD\Hot Wire Seal | 1.05 | 1.15 | 1.25 | 1.55 | ||||||||
| COF (Film To Film) | - | |||||||||||
| Static 静摩擦 | D1894 | 0.20 | 0.18 | 0.22 | 0.23 | |||||||
| Dynamic 动摩擦 | 0.20 | 0.18 | 0.22 | 0.23 | ||||||||
| OPTICS | ||||||||||||
| Haze 雾度 | D1003 | 3.5 | 3.8 | 4.0 | 4.3 | |||||||
| Clarity 透明度 | D1746 | 93.0 | 92.0 | 91.0 | 90.0 | |||||||
| Gloss @ 45Deg 光泽度 | D2457 | 85.0 | 82.0 | 80.0 | 81.0 | |||||||
| BARRIER 阻隔性 | ||||||||||||
| Oxygen Transmission Rate 透氧率 | cc/㎡/day | D3985 | 9200 | 8200 | 5600 | 4200 | ||||||
| Water Vapor Transmission Rate 透水气率 | gm/㎡/day | F1249 | 25.9 | 17.2 | 14.5 | 11.2 | ||||||
| SHRINKAGEPROPERTIES 收缩性 | MD | TD | MD | TD | ||||||||
| Free Shrinkage 收缩率 | 100℃ | % | D2732 | 17 | 26 | 14 | 23 | |||||
| 110℃ | 32 | 44 | 29 | 42 | ||||||||
| 120℃ | 54 | 59 | 53 | 60 | ||||||||
| 130℃ | 68 | 69 | 68 | 69 | ||||||||
| MD | MD | TD | TD | |||||||||
| Shrink Tension 收缩张力 | 100℃ | Mpa | D2838 | 1.65 | 2.35 | 1.70 | 2.25 | |||||
| 110℃ | 2.55 | 3.20 | 2.65 | 3.45 | ||||||||
| 120℃ | 2.70 | 3.45 | 2.95 | 3.65 | ||||||||
| 130℃ | 2.45 | 3.10 | 2.75 | 3.20 | ||||||||
Note:This information represents our best judgment on the work done, but the company assumes no liability whatsoever in connection with the use of information or findings contained herein.